Document Type : Original Article

Authors

1 Biomaterial Research Center, Dept. of Operative Dentistry, School of Dentistry, Shiraz University of Medical Sciences, Shiraz, Iran.

2 Postgraduate Student, Student Research Committee, Dept. of Operative Dentistry, School of Dentistry, Shiraz University of Medical Sciences, Shiraz, Iran.

Abstract

Statement of the Problem: Immediate application of bonding agent to home- bleached enamel leads to significant reduction in the shear bond strength of composite resin due to the residual oxygen. Different antioxidant agents may overcome this problem.Purpose: This study aimed to assess the effect of different antioxidants on the shear bond strength of composite resin to home-bleached.Materials and Method: Sixty extracted intact human incisors were embedded in cylindrical acrylic resin blocks (2.5×1.5 cm), with the coronal portion left out of the block. After bleaching the labial enamel surface with 15% carbamide peroxide, they were randomly divided into 6 groups (n=10). Before performing composite resin restoration by using a cylindrical Teflon mold (5×2 mm), each group was treated with one of the following antioxidants: 10% sodium ascorbate solution, 10% pomegranate peel solution, 10% grape seed extract, 5% green tea extract, and aloe vera leaf gel. One group was left untreated as the control. The shear bond strength of samples was tested under a universal testing machine (ZwickRoell Z020). The shear bond strength data were analyzed by one-way ANOVA and post hoc Tukey tests (p< 0.05).Results: No significant difference existed between the control and experimental groups. Moreover, there was no statistically significant difference between the effects of different antioxidants on the shear bond strength of bleached enamel.Conclusion: Different antioxidants used in this study had the same effect on the shear bond strength of home-bleached enamel, and none of them caused a statistically significant increase in its value.